    Chemical weathering of clay-rich sandstone matrix - control and case studies
Údaj o odpovědnosti
    Jana Soukupová, David Hradil, Richard Přikryl
Autor
    Hradil, David
    Přikryl, Richard, 1968-
    Soukupová, Jana
Jazyk
    anglicky
Zdrojový dokument - monografie
    Understanding and managing of stone decay : (SWAPNET 2001)
Strany
    s. 263-271
Poznámky
    4 obr., 1 fot., 1 tab., 19 bibl.
    il.
Předmětová skupina
    chemismus hornin
    česká křídová pánev
    jíl
    jizerský faciální vývoj
    křída-svrchní
    látky znečišťující
    lužický faciální vývoj
    ochrana přírody
    pískovce
    tmel
Geografické jméno
    ČR-Čechy
Klíčové slovo
    Case
    Chemical
    Clay-rich
    Control
    Matrix
    Sandstone
    Studies
    Weathering
Abstrakt (anglicky)
   The current research was focused on two aspects of sandstone decay: (i) mineralogical composition of neo-formed phases as the result of environmental conditions in regional scale and (ii) reaction of the clay matrix with sulphate-rich acid waters with respect to composition of the crusts on Cretaceous quartz sandstones of N and NW Bohemia is quite similar in all studied samples; gypsum and ammonium and/or potassium-rich alums are predominant phases. Except of aluminium, occurrence of all the main compounds forming the crusts (SO2-4, Ca2+, NH+4) is in good correlation with a typical composition of acid rain; while evaporating, gypsum is preferentially crystallized; ammonium alums are preferentially contamined by potassium. In agreement with our leaching experiments when hydrated aluminium silicate (halloysite) was reacted with 0.5M sulphuric acid solutions for 10 days, aluminium is released rather from poorly crystalline phases.
   release of aluminium is 4-5times faster in the case of smaller and disordered particles of halloysite if compared with iso-chemical well-ordered kaolinite platelets