Název
    Kinetics of the release of Silicon and Aluminium from Aluminosilicates into Aqueous Mildly Acid Solutions
Údaj o odpovědnosti
    Jiří Faimon
Autor
    Faimon, Jiří, 1950-
Jazyk
    anglicky
Zdrojový dokument - seriál
    Scripta facultatis scientiarum naturalium Universitatis Masarykianae brunensis
Svazek/č.
    Vol. 25
Strany
    p. 59-68
Rok
    1995
Poznámky
    4 obr., 5 tab., 2 s.bibl.
    Anglické resumé
    Zkr. název ser.: Scr. Univ. Masaryk. brun., Geol.
Předmětová skupina
    alumosilikáty
    amfibolit
    defekt povrchu krystalu
    granodiorit
    hliník
    kinematika
    křemík
    rozpustnost
    studie experimentální
    zvětrávání
    živce
Geografické jméno
    Brno-Řečkovice
    ČR-Morava
    Věžná (Žďár nad Sázavou)
    Želešice (Brno-venkov)
Klíčové slovo
    Acid
    Aluminium
    Aluminosilicates
    Aqueous
    Kinetics
    Mildly
    Release
    Silicon
    Solutions
Abstrakt (anglicky)
   The release of Si and Al from feldspar, granodiorite and amphibolite into mildly acid solutions was investigated during long-term laboratory batch experiments. A simple kinetic model, including dissolution of surface defects and precipitation of secondary solids, was proposed. The rate constans for fluxes of Si and Al in and out from solution were estimated on the basis of the model. They are summarized as follow: Si fluxes into solution ( mol.m-2 day-1): feldspar 1.35, granodiorite 2.18, amphibolite 5.57; Al fluxes into solution ( mol.m-2 day-1): feldspar 3.75, granodiorite 1.14, amphibolite 0.18; Ai fluxes out away from solution (day-1): feldspar 6.3x10-3, granodiorite 7.4x10-3, amphibolite 2.3x10-2; Al fluxes out away from solution (day-1): feldspar 4.3x10-2, granodiorite 1.2x10-1, amphibolite 1.6x10-1. The fluxes of silicon from the aluminosilicates increase in the sequence feldspar - granodiorite - amphibolite. The fluxes of aluminium seem to follow the opposite trend.
   The release of Si and Al from feldspar is non-stechiometric. The fluxes of Al from solution into secondary solids greatly exceed the fluxes of Si