Název
    Large scale melt synthesis in an open crucible of Na-fluorohectorite with superb charge homogeneity and particle size
Autor
    Breu, Josef
    Dolejš, David
    Kalo, Hussein
    Moller, Michael W.
    Ziadeh, Mazen
Jazyk
    anglicky
Typ dokumentu
    článek v periodiku
Zdrojový dokument - seriál
    Applied Clay Science
Svazek/č.
    Roč. 48, č. 1-2
Strany
    7
Rok
    2010
Výraz tezauru
    melt
    Na-fluorohectorite
    synthesis
Klíčové slovo
    Charge
    Crucible
    Homogeneity
    Large
    Melt
    Na-fluorohectorite
    Open
    Particle
    Scale
    Size
    Superb
    Synthesis
Abstrakt (anglicky)
   Sodium fluorohectorite Na-0.6[Mg2.4Li0.6]Si4O10F2 was synthesized from the melt in an open glassy carbon crucible at 1265 degrees C under argon flow. A glass (Na2O-Li2O-SiO2) precursor was used as a fluxing agent in order to maintain a low vapor pressure of volatile fluorides and sustain a low silica activity, which inhibits the formation of silicon fluoride gases and promotes the fluorine solubility in the melt.