Název
    Natural SnGeS3 from Radvanice near Trutnov (Czech Republic): its description, crystal structure refinement and solid solution with PbGeS3
Údaj o odpovědnosti
    Jiří Sejkora, Peter Berlepsch, Emil Makovicky, Tonči Balić-Žunić
Autor
    Balić-Žunić, Tonči
    Berlepsch, Peter
    Makovicky, Emil
    Sejkora, Jiří, 1968-
Jazyk
    anglicky
Zdrojový dokument - seriál
    European journal of mineralogy
Svazek/č.
    Vol. 13, no. 4
Strany
    p. 791-800
Rok
    2001
Poznámky
    5 obr., 2 fot., 8 tab., 21 bibl.
    il.
    Zkr. název ser.: Eur. J. Mineral.
Předmětová skupina
    chemismus minerálů
    cín
    germanium
    minerály hořící haldy
    minerály supergenní
    olovo
    redukce
    roztok pevný
    sulfidy
    vnitrosudetská pánev
    zpřesňování struktury
Geografické jméno
    ČR-Čechy
    Radvanice (Trutnov)
Klíčové slovo
    Crystal
    Czech
    Description
    Natural
    Near
    PbGeS3
    Radvanice
    Refinement
    Republic
    SnGeS3
    Solid
    Solution
    Structure
    Trutnov
Abstrakt (anglicky)
   Natural SnGeS3 is monoclinic, with space group P21/c and with a = 7.2704(15)A, b = 10197(2)A, c = 6.8463(14)A, á = 105.34(3)ř, V = 489.5 A3, a:b:c = 0.7130:1:0.6714, Z = 4 and Dcalc = 3.98 g/cm3. The strongest lines in the X-ray powder diffraction pattern are (d in A/I/I0 (hkl)) : 7.006/100 (100), 4.135/49 (120), 3.077/47 (130), 2.776/38 (022), 2.699/69 (211), 2.121/31 (320), 1.724/35 (41-2). it forms transparent, elastic and flexible flattened acicular crystals with cross-section 2-5 x 20-40 um and up to 1 cm in the length, which produce random or fan-shaped clusters on rock fragments and on black crumbly ash. It has an orange to yellowish red colour, very light yellowish brown streak, vitreous to adamantine lustre; VHN 10g microhardness is 55 kp/mmř (539 MPa); two types of perfect cleavage were established - perpendicular or oblique to elongation. No fluorescence at 254 and 366 nm of UV light was observed.
   In reflected light SnGeS3 is light grevish white with distinct orange brown internal reflections, anisotropic rotation tints are from dark brownish grey to reddish brown or brownnish violet. Chemical analysis yields an average composition of Sn 40.47, Pb 0.29, Ge 22.73, Fe 0.03, Bi 0.27, Sb 0.10, As 0.10, S 31.42, Se 2.62, total 98.03 wt.%, leading to an empirical formula Sn 1.02 Ge 0.94 (S 2.93 Se 0.10) 0.03. SnGeS3 was also observed in multicomponent aggregates on which the above described acicular crystals grow. Phases of the SnGeS3-PbGeS3 series in these aggregates from irregular grains 2-100 um size with a more variable composition
Přispěvatel